| Material | HDPE/LDPE/LLDPE |
| Width | 2-8m |
| Roll Size | 6x50/6x100m |
| Thickness | 0.1-3.0mm |
| Color | Black, white or as customers' required. |
| Standard | ASTM, CE certification, ISO standard, GB/T, CJ/T, JT/T, TB/T, JC, etc. |
| Function | High mechanical strength, puncture resistance, UV resistance, anti-aging, and so on. |
| Application | environmental protection and environmental sanitation, water conservancy, municipal projects, landscape garden, petrochemical industry, mine industry, traffic facilities, agriculture, aquiculture industry, salt industry and so on. |
Production Performance Feature:
1.Resist aging performance: HDPE film has high quality of resist aging, ultraviolet and decompose, can be used in the air. The life-span of material Can reach 50-70 years providing guarantee for environmental anti-seepage.
2.Resist plant root: HDPE film has good anti-puncture ability, can against almost plant foots.
3. High machine strength: HDPE film has excellent flexibility and distortion, can adapt un-even sedimentation. Extend strength is 28MP, elongation at break is 700%.
4.Good benefit: new technology improved HDPE film's anti-seepage, low the cost compare with the additional material .via practical testing, HDPE Geomembrane can save 50% project cost
5.Fast construction: HDPE film has high flexibility, multi-specification and pave forms, can cater for different engineering demand.
| No. | Item | Value | |||
| General GH-1 | ECO GH-2 | CJ/T | ASTM | ||
| 1 | Thickness mm | 0.75 | 1.0 | 1.5 | 2.0 |
| 2 | Width m | 2.5~8 | |||
| 3 | Tensile Strength (TD/MD) Mpa | 21(KN/M) | 28(KN/M) | 43(KN/M) | 57(KN/M) |
| 4 | Elongation at Break (TD/MD) % | ≥750 | |||
| 5 | Strength at Tear (Right-angle Tear) N/mm | 112 | 156 | 222 | 289 |
| 6 | Carbon Black Content % | 2.0-3.0 | |||
| 7 | Anti-crack F20, H | ≥1500 | |||
| 8 | -70ºC Low Temperature Impact Brittle Property | pass | pass | ||
| 9 | Oxidative Inducement Time at 200ºC, min | ≥20 | |||